| 品牌 | 沙伯基础 SABIC |
|---|---|
| 货号 | HDPE CC3054 |
| 用途 | 工程应用 |
| 特性级别 | 阻燃级|||增韧级|||增强级|||透明级|||热稳定性|||耐高温|||耐低温|||抗紫外线|||导电级|||标准级|||耐水解|||耐老化|||耐候|||抗静电|||抗化学性|||高强度|||高流动|||高结晶（HCPP）|||高滑动|||高光泽|||高刚性|||粉料||| |
| 牌号 | HDPE CC3054 |
| 型号 | HDPE CC3054 |
| 加工级别 | 注塑级|||中空级|||涂覆级|||热熔级|||拉丝级|||挤出级|||滚塑级|||吹塑级|||压延|||脱模级|||喷涂|||模塑|||吹膜级|||包覆||| |
| 品名 | HDPE |
| 外形尺寸 | 来电询问 |
| 用途级别 | 通用级|||食品级|||汽车部件|||光学级|||管材级|||电子电器部件|||薄膜级|||板材级|||照明灯具|||运动器材|||医用级|||型材|||纤维|||瓶盖专用料|||流延膜专用料|||家电部件|||电线电缆级|||电动工具配件|||薄壁制品||| |
| 生产企业 | 沙伯基础 SABIC |
| 是否进口 | 是 |
SABIC® HDPE CC3054
SABIC® HDPE CC3054 is a high density polyethylene copolymer injection molding grade. Its narrow molecular weight distribution and high flow results in low warpage, good rigidity, good gloss and fast molding cycles.
SABIC® HDPE CC3054 is typically used for caps and closures applications and thin wall articles.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
HDPE CC3054 沙伯基础 SABIC
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
0.954
|
g/cm3
|
ISO 1183 |
|
熔流率（熔体流动速率） (190°C/2.16 kg)
|
30
|
g/10 min
|
ISO 1133 |
|
抗环境应力开裂 1 (40°C, 1.00 mm, 10% Igepal CO-630, 模压成型)
|
10.0
|
hr
|
内部方法 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 模压成型)
|
61
|
|
ISO 868 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 (2.00 mm, 模压成型)
|
1100
|
MPa
|
ISO 527-1/1BA/50 |
|
拉伸应力
|
ISO 527-2/1BA/50 | ||
|
屈服, 2.00 mm, 模压成型
|
26.0
|
MPa
|
|
|
断裂, 2.00 mm, 模压成型
|
25.0
|
MPa
|
|
|
拉伸应变 (断裂, 2.00 mm, 模压成型)
|
200
|
%
|
ISO 527-2/1BA/50 |
|
弯曲模量 (模压成型)
|
1250
|
MPa
|
ISO 178 |
|
弯曲应力 (模压成型)
|
27.0
|
MPa
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C, 模压成型)
|
3.0
|
kJ/m2
|
ISO 180/A |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 2 (0.45 MPa, 未退火)
|
82.0
|
°C
|
ISO 75-2/B |
|
维卡软化温度 2
|
125
|
°C
|
ISO 306/A |
|
熔融温度
|
132
|
°C
|
ISO 11357-3 |
|
Enthalpy Change
|
205
|
J/g
|
ISO 11357-3 |